Sabic Lexan ML7555 PRELIMINARY DATA. Internal Mold Release: UV-Stabilized And Flame Retardant

100KG
MOQ
*USD
Price
Sabic Lexan ML7555 PRELIMINARY DATA. Internal Mold Release: UV-Stabilized And Flame Retardant
Features Gallery Product Description Request A Quote
Features
Specifications
Melt Flow Rate, 300°C/1.2 Kgf: 11.2
Basic Infomation
Place of Origin: ——
Brand Name: Sabic Lexan
Certification: COA/ICP Test/Rohs/MSDS
Model Number: ML7555
Payment & Shipping Terms
Packaging Details: 25KG/BAG
Delivery Time: To be negotiated
Payment Terms: L/C, T/T, Western Union, MoneyGram
Supply Ability: To be negotiated
Product Description

Sabic Lexan  ML7555 resin is PRELIMINARY DATA. Internal mold release: UV-stabilized and flame retardant


Property

TYPICAL PROPERTIES (1)      
MECHANICAL Value Unit Standard
Tensile Stress, yld, Type I, 50 mm/min 58 MPa ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min 61 MPa ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min 90 % ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span 88 MPa ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span 2060 MPa ASTM D 790
IMPACT Value Unit Standard
Izod Impact, notched, 23°C 801 J/m ASTM D 256
Izod Impact, notched, -50°C 587 J/m ASTM D 256
Izod Impact, notched, 23°C, 6.4mm 640 J/m ASTM D 256
Izod Impact, double-gated, 23°C 1068 J/m SABIC Method
Instrumented Impact Energy @ peak, 23°C 52 J ASTM D 3763
THERMAL Value Unit Standard
HDT, 1.82 MPa, 6.4 mm, unannealed 124 °C ASTM D 648
Relative Temp Index, Elec 50 °C UL 746B
Relative Temp Index, Mech w/impact 50 °C UL 746B
Relative Temp Index, Mech w/o impact 50 °C UL 746B
PHYSICAL Value Unit Standard
Melt Flow Rate, 300°C/1.2 kgf 11.2 g/10 min ASTM D 1238
ELECTRICAL Value Unit Standard
Hot Wire Ignition {PLC) 1 PLC Code UL 746A
High Ampere Arc Ign, surface {PLC} 0 PLC Code UL 746A
Comparative Tracking Index (UL) {PLC} 3 PLC Code UL 746A
FLAME CHARACTERISTICS Value Unit Standard
UL Recognized, 94V-0 Flame Class Rating (3) 1.49 mm UL 94
UL Recognized, 94-5VA Rating (3) 2.99 mm UL 94
Source GMD, last updated:01/04/2000    

Processing

Parameter    
Injection Molding Value Unit
Drying Temperature 105 - 110 °C
Drying Time 3 - 4 hrs
Drying Time (Cumulative) 24 hrs
Melt Temperature 260 - 305 °C
Nozzle Temperature 255 - 300 °C
Front - Zone 3 Temperature 260 - 305 °C
Middle - Zone 2 Temperature 250 - 295 °C
Rear - Zone 1 Temperature 240 - 280 °C
Mold Temperature 50 - 80 °C
Back Pressure 0.3 - 0.7 MPa
Screw Speed 35 - 75 rpm
Shot to Cylinder Size 40 - 60 %
Vent Depth 0.038 - 0.076 mm
Source GMD, last updated:01/04/2000  
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.    
PLEASE CHECK WITH YOUR (LOCAL SALES OFFICE) FOR AVAILABILITY IN YOUR REGION  
(1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours
storage at 23°C/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded
samples. All samples tested under ISO test standards are prepared according to ISO 294.
(2) Only typical data for selection purposes. Not to be used for part or tool design.    
(3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.  
(4) Internal measurements according to UL standards.    

 


 

For more information please download the datasheet

Sabic Lexan ML7555 PRELIMINARY DATA. Internal Mold Release: UV-Stabilized And Flame Retardant 0  Sabic Lexan ML7555.pdf

 

Get The Latest Quotation

 

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

 

Sabic Lexan ML7555 PRELIMINARY DATA. Internal Mold Release: UV-Stabilized And Flame Retardant 1Click to consult and get the latest quotation within 24 hours!

 

sabic lexan pc products

 

Free Talk 24hours

Recommended Products
Get in touch with us
Tel : 86-13925273675
Characters Remaining(20/3000)