Sabic Lexan IFX6420Z Is A Medium Viscosity, Release Containing, Injection Moldable, Polycarbonate Grade

100KG
MOQ
*USD
Price
Sabic Lexan IFX6420Z Is A Medium Viscosity, Release Containing, Injection Moldable, Polycarbonate Grade
Features Gallery Product Description Request A Quote
Features
Specifications
Melt Flow Rate, 300°C/1.2 Kgf: 12.5
Basic Infomation
Place of Origin: ——
Brand Name: Sabic Lexan
Certification: COA/ICP Test/Rohs/MSDS
Model Number: IFX6420Z
Payment & Shipping Terms
Packaging Details: 25KG/BAG
Delivery Time: To be negotiated
Payment Terms: L/C, T/T, Western Union, MoneyGram
Supply Ability: To be negotiated
Product Description

Sabic Lexan  IFX6420Z resin is a medium viscosity, release containing, injection moldable, polycarbonate grade suitable for use in industry protectiveeye-ware welding applications. This grades meets the transmission and haze requirements per ANSI 87.1 norm, Scale 6 when molded at


Property

TYPICAL PROPERTIES (1)      
MECHANICAL Value Unit Standard
Tensile Stress, yld, Type I, 50 mm/min 62 MPa ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min 65 MPa ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min 7 % ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min 110 % ASTM D 638
Tensile Modulus, 5 mm/min 2400 MPa ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span 93 MPa ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span 2300 MPa ASTM D 790
Tensile Stress, yield, 50 mm/min 65 MPa ISO 527
Tensile Stress, break, 50 mm/min 70 MPa ISO 527
Tensile Strain, yield, 50 mm/min 6 % ISO 527
Tensile Strain, break, 50 mm/min 120 % ISO 527
Tensile Modulus, 1 mm/min 2350 MPa ISO 527
Flexural Stress, yield, 2 mm/min 90 MPa ISO 178
Flexural Modulus, 2 mm/min 2250 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact, notched, 23°C 850 J/m ASTM D 256
Izod Impact, notched, -30°C 135 J/m ASTM D 256
Instrumented Impact Total Energy, 23°C 65 J ASTM D 3763
Izod Impact, unnotched 80*10*3 +23°C NB kJ/m² ISO 180/1U
Izod Impact, unnotched 80*10*3 -30°C NB kJ/m² ISO 180/1U
Izod Impact, notched 80*10*3 +23°C 70 kJ/m² ISO 180/1A
Izod Impact, notched 80*10*3 -30°C 12 kJ/m² ISO 180/1A
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm 73 kJ/m² ISO 179/1eA
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm 14 kJ/m² ISO 179/1eA
Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm NB kJ/m² ISO 179/1eU
Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm NB kJ/m² ISO 179/1eU
THERMAL Value Unit Standard
Vicat Softening Temp, Rate B/50 154 °C ASTM D 1525
HDT, 1.82 MPa, 6.4 mm, unannealed 132 °C ASTM D 648
CTE, -40°C to 40°C, flow 7.E-05 1/°C ASTM E 831
CTE, -40°C to 40°C, xflow 7.E-05 1/°C ASTM E 831
CTE, -40°C to 40°C, flow 7.E-05 1/°C ISO 11359-2
CTE, -40°C to 40°C, xflow 7.E-05 1/°C ISO 11359-2
Vicat Softening Temp, Rate B/50 141 °C ISO 306
Vicat Softening Temp, Rate B/120 142 °C ISO 306
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm 123 °C ISO 75/Af
PHYSICAL Value Unit Standard
Specific Gravity 1.2 - ASTM D 792
Mold Shrinkage, flow, 3.2 mm 0.5 - 0.7 % SABIC Method
Melt Flow Rate, 300°C/1.2 kgf 12.5 g/10 min ASTM D 1238
Density 1.2 g/cm³ ISO 1183
Water Absorption, (23°C/sat) 0.35 % ISO 62
Moisture Absorption (23°C / 50% RH) 0.15 % ISO 62
Melt Volume Rate, MVR at 300°C/1.2 kg 12 cm³/10 min ISO 1133
Source GMD, last updated:2009/04/22    

Processing

Parameter    
Injection Molding Value Unit
Drying Temperature 120 °C
Drying Time 3 - 4 hrs
Drying Time (Cumulative) 48 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 295 - 315 °C
Nozzle Temperature 290 - 310 °C
Front - Zone 3 Temperature 295 - 315 °C
Middle - Zone 2 Temperature 280 - 305 °C
Rear - Zone 1 Temperature 270 - 295 °C
Mold Temperature 70 - 95 °C
Back Pressure 0.3 - 0.7 MPa
Screw Speed 40 - 70 rpm
Shot to Cylinder Size 40 - 60 %
Vent Depth 0.025 - 0.076 mm
Source GMD, last updated:2009/04/22  

 


 

For more information please download the datasheet

Sabic Lexan IFX6420Z Is A Medium Viscosity, Release Containing, Injection Moldable, Polycarbonate Grade 0  Sabic Lexan IFX6420Z.pdf

 

Get The Latest Quotation

 

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

 

Sabic Lexan IFX6420Z Is A Medium Viscosity, Release Containing, Injection Moldable, Polycarbonate Grade 1Click to consult and get the latest quotation within 24 hours!

 

sabic lexan pc products

 

Free Talk 24hours

Recommended Products
Get in touch with us
Tel : 86-13925273675
Characters Remaining(20/3000)