Sabic Lexan FXE1810T polycarbonate (PC) siloxane copolymer resin is a transparent injection moldable grade

100KG
MOQ
*USD
Price
Sabic Lexan FXE1810T polycarbonate (PC) siloxane copolymer resin is a transparent injection moldable grade
Features Gallery Product Description Request A Quote
Features
Specifications
Melt Flow Rate, 300°C/1.2 Kgf: 35
Basic Infomation
Place of Origin: ——
Brand Name: Sabic Lexan
Certification: COA/ICP Test/Rohs/MSDS
Model Number: FXE1810T
Payment & Shipping Terms
Packaging Details: 25KG/BAG
Delivery Time: To be negotiated
Payment Terms: L/C, T/T, Western Union, MoneyGram
Supply Ability: To be negotiated
Product Description

Sabic Lexan  FXE1810T resin is polycarbonate (PC) siloxane copolymer resin is a transparent injection moldable grade. This specialty PC offers excellent processability, very high flow and improved ductility characteristics over standard PC.Lexan FXE1810T resin may be an excellent candidate for a wide variety of applications.This product is available in the Visual fX* Piano Black, Raven Black & Illuminate color range only.


Property

MECHANICAL Value Unit Standard
Tensile Stress, yld, Type I, 50 mm/min 59 MPa ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min 58 MPa ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min 5.7 % ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min 118.9 % ASTM D 638
Tensile Modulus, 50 mm/min 2360 MPa ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span 99 MPa ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span 2350 MPa ASTM D 790
Tensile Stress, yield, 50 mm/min 59 MPa ISO 527
Tensile Stress, break, 50 mm/min 56 MPa ISO 527
Tensile Strain, yield, 50 mm/min 5.4 % ISO 527
Tensile Strain, break, 50 mm/min 118.6 % ISO 527
Tensile Modulus, 1 mm/min 2400 MPa ISO 527
Flexural Stress, yield, 2 mm/min 92 MPa ISO 178
Flexural Modulus, 2 mm/min 2250 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact, notched, 23°C 702 J/m ASTM D 256
Izod Impact, notched, -30°C 220 J/m ASTM D 256
Instrumented Impact Total Energy, 23°C 79 J ASTM D 3763
Izod Impact, unnotched 80*10*3 +23°C NB kJ/m² ISO 180/1U
Izod Impact, unnotched 80*10*3 -30°C NB kJ/m² ISO 180/1U
Izod Impact, notched 80*10*3 +23°C 60 kJ/m² ISO 180/1A
Izod Impact, notched 80*10*3 -30°C 30 kJ/m² ISO 180/1A
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm 65 kJ/m² ISO 179/1eA
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm 40 kJ/m² ISO 179/1eA
Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm NB kJ/m² ISO 179/1eU
Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm NB kJ/m² ISO 179/1eU
THERMAL Value Unit Standard
Vicat Softening Temp, Rate A/50 138 °C ASTM D 1525
HDT, 1.82 MPa, 3.2mm, unannealed 120 °C ASTM D 648
CTE, -40°C to 95°C, flow 6.5E-05 1/°C ASTM E 831
CTE, -40°C to 95°C, xflow 7.4E-05 1/°C ASTM E 831
CTE, 23°C to 80°C, flow 6.5E-05 1/°C ISO 11359-2
CTE, 23°C to 80°C, xflow 7.4E-05 1/°C ISO 11359-2
Vicat Softening Temp, Rate B/50 137 °C ISO 306
Vicat Softening Temp, Rate B/120 140 °C ISO 306
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm 117 °C ISO 75/Af
PHYSICAL Value Unit Standard
Specific Gravity 1.19 - ASTM D 792
Mold Shrinkage, flow, 3.2 mm 0.4 - 0.8 % SABIC Method
Melt Flow Rate, 300°C/1.2 kgf 35 g/10 min ASTM D 1238
Density 1.19 g/cm³ ISO 1183
Water Absorption, (23°C/sat) 0.24 % ISO 62
Moisture Absorption (23°C / 50% RH) 0.09 % ISO 62
Melt Volume Rate, MVR at 300°C/1.2 kg 33 cm³/10 min ISO 1133
Source GMD, last updated:09/29/2005    

Processing

Parameter    
Injection Molding Value Unit
Drying Temperature 120 °C
Drying Time 3 - 4 hrs
Drying Time (Cumulative) 48 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 295 - 315 °C
Nozzle Temperature 290 - 310 °C
Front - Zone 3 Temperature 295 - 315 °C
Middle - Zone 2 Temperature 280 - 305 °C
Rear - Zone 1 Temperature 270 - 295 °C
Mold Temperature 70 - 95 °C
Back Pressure 0.3 - 0.7 MPa
Screw Speed 40 - 70 rpm
Shot to Cylinder Size 40 - 60 %
Vent Depth 0.025 - 0.076 mm
Source GMD, last updated:09/29/2005  

 


 

For more information please download the datasheet

Sabic Lexan FXE1810T polycarbonate (PC) siloxane copolymer resin is a transparent injection moldable grade 0  Sabic Lexan FXE1810T.pdf

 

Get The Latest Quotation

 

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

 

Sabic Lexan FXE1810T polycarbonate (PC) siloxane copolymer resin is a transparent injection moldable grade 1Click to consult and get the latest quotation within 24 hours!

 

sabic lexan pc products

 

Free Talk 24hours

Recommended Products
Get in touch with us
Tel : 86-13925273675
Characters Remaining(20/3000)