Sabic Lexan ML7397 UV-Stabilized, Co-Extrusion Capstock Polycarbonate Resin For Sheet Extrusin Applications

100KG
MOQ
*USD
Price
Sabic Lexan ML7397 UV-Stabilized, Co-Extrusion Capstock Polycarbonate Resin For Sheet Extrusin Applications
Features Gallery Product Description Request A Quote
Features
Specifications
Melt Flow Rate, 300°C/1.2 Kgf: 5
Basic Infomation
Place of Origin: ——
Brand Name: Sabic Lexan
Certification: COA/ICP Test/Rohs/MSDS
Model Number: ML7397
Payment & Shipping Terms
Packaging Details: 25KG/BAG
Delivery Time: To be negotiated
Payment Terms: L/C, T/T, Western Union, MoneyGram
Supply Ability: To be negotiated
Product Description

Sabic Lexan  ML7397 resin is UV-stabilized, co-extrusion capstock Polycarbonate resin for sheet extrusin applications.


Property

TYPICAL PROPERTIES (1)      
MECHANICAL Value Unit Standard
Tensile Stress, yld, Type I, 50 mm/min 71 MPa ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min 73 MPa ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min 5 % ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min 98 % ASTM D 638
Tensile Modulus, 5 mm/min 2600 MPa ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span 105 MPa ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span 2600 MPa ASTM D 790
IMPACT Value Unit Standard
Izod Impact, notched, 23°C 91 J/m ASTM D 256
THERMAL Value Unit Standard
HDT, 1.82 MPa, 3.2mm, unannealed 114 °C ASTM D 648
PHYSICAL Value Unit Standard
Specific Gravity 1.19 - ASTM D 792
Melt Flow Rate, 300°C/1.2 kgf 5 g/10 min ASTM D 1238
Source GMD, last updated:2010/06/28    

Processing

Parameter      
Profile Extrusion Value Unit  
Drying Temperature 120 °C  
Drying Time 2 - 4 hrs  
Maximum Moisture Content 0.02 %  
Melt Temperature 270 - 280 °C  
Barrel - Zone 1 Temperature 260 - 280 °C  
Barrel - Zone 2 Temperature 260 - 280 °C  
Barrel - Zone 3 Temperature 260 - 280 °C  
Barrel - Zone 4 Temperature 260 - 280 °C  
Hopper Temperature 40 - 60 °C  
Adapter Temperature 260 - 280 °C  
Die Temperature 250 - 260 °C  
Calibrator Temperature 70 - 90 °C  
Source GMD, last updated:2010/06/28    
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.    
PLEASE CHECK WITH YOUR (LOCAL SALES OFFICE) FOR AVAILABILITY IN YOUR REGION    
(1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours
storage at 23°C/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded
samples. All samples tested under ISO test standards are prepared according to ISO 294.
(2) Only typical data for selection purposes. Not to be used for part or tool design.  
(3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.      
(4) Internal measurements according to UL standards.      
(5) Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing
conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or
legacy tooling prior to cutting tools for new molded article.
     

 


 

For more information please download the datasheet

Sabic Lexan ML7397 UV-Stabilized, Co-Extrusion Capstock Polycarbonate Resin For Sheet Extrusin Applications 0  Sabic Lexan ML7397.pdf

 

Get The Latest Quotation

 

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

 

Sabic Lexan ML7397 UV-Stabilized, Co-Extrusion Capstock Polycarbonate Resin For Sheet Extrusin Applications 1Click to consult and get the latest quotation within 24 hours!

 

sabic lexan pc products

 

Free Talk 24hours

Recommended Products
Get in touch with us
Tel : 86-13925273675
Characters Remaining(20/3000)