Sabic Lexan FXE154R Is A Transparent/Translucent High Viscosity Polycarbonate Resin With A Branched Molecular

100KG
MOQ
*USD
Price
Sabic Lexan FXE154R Is A Transparent/Translucent High Viscosity Polycarbonate Resin With A Branched Molecular
Features Gallery Product Description Request A Quote
Features
Specifications
Melt Volume Rate, MVR At 300°C/2.16 Kg: 4
UL Compliant, 94V-2 Flame Class Rating (3)(4): 1.6
Basic Infomation
Place of Origin: ——
Brand Name: Sabic Lexan
Certification: COA/ICP Test/Rohs/MSDS
Model Number: FXE154R
Payment & Shipping Terms
Packaging Details: 25KG/BAG
Delivery Time: To be negotiated
Payment Terms: L/C, T/T, Western Union, MoneyGram
Supply Ability: To be negotiated
Product Description

Sabic Lexan  FXE154R resin is a transparent/translucent high viscosity polycarbonate resin with a branched molecular structure for extrusion and blow molding and is complying with FDA regulations. The grade is designed for special effects with fluorescent appearance. Color
package may affect performance.


Property

MECHANICAL Value Unit Standard
Tensile Stress, yield, 50 mm/min 60 MPa ISO 527
Tensile Stress, break, 50 mm/min 65 MPa ISO 527
Tensile Strain, yield, 50 mm/min 7 % ISO 527
Tensile Strain, break, 50 mm/min 120 % ISO 527
Tensile Modulus, 1 mm/min 2350 MPa ISO 527
Flexural Stress, yield, 2 mm/min 100 MPa ISO 178
Flexural Modulus, 2 mm/min 2300 MPa ISO 178
Hardness, H358/30 95 MPa ISO 2039-1
IMPACT Value Unit Standard
Izod Impact, unnotched 80*10*3 +23°C NB kJ/m² ISO 180/1U
Izod Impact, unnotched 80*10*3 -30°C NB kJ/m² ISO 180/1U
Izod Impact, notched 80*10*3 +23°C 65 kJ/m² ISO 180/1A
Izod Impact, notched 80*10*3 -30°C 13 kJ/m² ISO 180/1A
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm 70 kJ/m² ISO 179/1eA
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm 16 kJ/m² ISO 179/1eA
Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm NB kJ/m² ISO 179/1eU
Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm NB kJ/m² ISO 179/1eU
THERMAL Value Unit Standard
Thermal Conductivity 0.2 W/m-°C ISO 8302
CTE, 23°C to 80°C, flow 7.E-05 1/°C ISO 11359-2
Ball Pressure Test, 125°C +/- 2°C PASSES - IEC 60695-10-2
Vicat Softening Temp, Rate B/50 146 °C ISO 306
Vicat Softening Temp, Rate B/120 143 °C ISO 306
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm 124 °C ISO 75/Ae
PHYSICAL Value Unit Standard
Mold Shrinkage on Tensile Bar, flow (2) 0.5 - 0.7 % SABIC Method
Density 1.2 g/cm³ ISO 1183
Water Absorption, (23°C/sat) 0.35 % ISO 62
Moisture Absorption (23°C / 50% RH) 0.15 % ISO 62
Melt Volume Rate, MVR at 300°C/2.16 kg 4 cm³/10 min ISO 1133
ELECTRICAL Value Unit Standard
Volume Resistivity >1.E+15 Ohm-cm IEC 60093
Surface Resistivity, ROA >1.E+15 Ohm IEC 60093
Dielectric Strength, in oil, 3.2 mm 17 kV/mm IEC 60243-1
FLAME CHARACTERISTICS Value Unit Standard
UL Compliant, 94V-2 Flame Class Rating (3)(4) 1.6 mm UL 94 by GE
Glow Wire Flammability Index 850°C, passes at 1 mm IEC 60695-2-12
Source GMD, last updated:11/26/2002    

Processing

Parameter    
Profile Extrusion Value Unit
Drying Temperature 120 °C
Drying Time 2 - 3 hrs
Melt Temperature 260 - 280 °C
Barrel - Zone 1 Temperature 280 - 320 °C
Barrel - Zone 2 Temperature 280 - 300 °C
Barrel - Zone 3 Temperature 260 - 280 °C
Barrel - Zone 4 Temperature 260 - 280 °C
Hopper Temperature 60 - 80 °C
Adapter Temperature 260 - 280 °C
Die Temperature 245 - 290 °C
Calibrator Temperature 80 - 120 °C
Source GMD, last updated:11/26/2002  

 


 

For more information please download the datasheet

Sabic Lexan FXE154R Is A Transparent/Translucent High Viscosity Polycarbonate Resin With A Branched Molecular 0  Sabic Lexan FXE154R.pdf

 

Get The Latest Quotation

 

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

 

Sabic Lexan FXE154R Is A Transparent/Translucent High Viscosity Polycarbonate Resin With A Branched Molecular 1Click to consult and get the latest quotation within 24 hours!

 

sabic lexan pc products

 

Free Talk 24hours

Recommended Products
Get in touch with us
Tel : 86-13925273675
Characters Remaining(20/3000)