Sabic Lexan 2814R A High Viscosity, 10% Glass Reinforced, Flame Retardant Grade,Especially Developed To Meet The CSTB

100KG
MOQ
*USD
Price
Sabic Lexan 2814R A High Viscosity, 10% Glass Reinforced, Flame Retardant Grade,Especially Developed To Meet The CSTB
Features Gallery Product Description Request A Quote
Features
Specifications
Melt Volume Rate, MVR At 300°C/1.2 Kg: 6
UL Recognized, 94V-0 Flame Class Rating (3): 1.5
Basic Infomation
Place of Origin: ——
Brand Name: Sabic Lexan
Certification: COA/ICP Test/Rohs/MSDS
Model Number: 2814R
Payment & Shipping Terms
Packaging Details: 25KG/BAG
Delivery Time: To be negotiated
Payment Terms: L/C, T/T, Western Union, MoneyGram
Supply Ability: To be negotiated
Product Description

Sabic Lexan  2814R resin is a high viscosity, 10% glass reinforced, flame retardant grade, especially developed to meet the CSTB M2 flammability rating.


Property

TYPICAL PROPERTIES (1)      
MECHANICAL Value Unit Standard
Taber Abrasion, CS-17, 1 kg 11 mg/1000cy SABIC Method
Tensile Stress, yield, 5 mm/min 60 MPa ISO 527
Tensile Stress, break, 5 mm/min 45 MPa ISO 527
Tensile Strain, yield, 5 mm/min 5 % ISO 527
Tensile Strain, break, 5 mm/min 7 % ISO 527
Tensile Modulus, 1 mm/min 3300 MPa ISO 527
Flexural Stress, break, 2 mm/min 95 MPa ISO 178
Flexural Modulus, 2 mm/min 3400 MPa ISO 178
Hardness, H358/30 130 MPa ISO 2039-1
IMPACT Value Unit Standard
Izod Impact, unnotched 80*10*3 +23°C NB kJ/m² ISO 180/1U
Izod Impact, unnotched 80*10*3 -30°C 110 kJ/m² ISO 180/1U
Izod Impact, notched 80*10*3 +23°C 8 kJ/m² ISO 180/1A
Izod Impact, notched 80*10*3 -30°C 7 kJ/m² ISO 180/1A
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm 8 kJ/m² ISO 179/1eA
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm 7 kJ/m² ISO 179/1eA
Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm NB kJ/m² ISO 179/1eU
Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm NB kJ/m² ISO 179/1eU
Charpy Impact, notched, 23°C 10 kJ/m² ISO 179/2C
Charpy Impact, notched, -20°C 4 kJ/m² ISO 179/2C
THERMAL Value Unit Standard
Thermal Conductivity 0.18 W/m-°C ISO 8302
CTE, 23°C to 80°C, flow 3.4E-05 1/°C ISO 11359-2
Ball Pressure Test, 125°C +/- 2°C PASSES - IEC 60695-10-2
Vicat Softening Temp, Rate A/50 150 °C ISO 306
Vicat Softening Temp, Rate B/50 141 °C ISO 306
Vicat Softening Temp, Rate B/120 143 °C ISO 306
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm 140 °C ISO 75/Be
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm 132 °C ISO 75/Ae
Relative Temp Index, Elec 80 °C UL 746B
Relative Temp Index, Mech w/impact 80 °C UL 746B
Relative Temp Index, Mech w/o impact 80 °C UL 746B
PHYSICAL Value Unit Standard
Mold Shrinkage on Tensile Bar, flow (2) 0.2 - 0.6 % SABIC Method
Density 1.25 g/cm³ ISO 1183
Water Absorption, (23°C/sat) 0.31 % ISO 62
Moisture Absorption (23°C / 50% RH) 0.13 % ISO 62
Melt Volume Rate, MVR at 300°C/1.2 kg 6 cm³/10 min ISO 1133
OPTICAL Value Unit Standard
Haze NA % ASTM D 1003
Refractive Index NA - ISO 489
ELECTRICAL Value Unit Standard
Volume Resistivity >1.E+15 Ohm-cm IEC 60093
Surface Resistivity, ROA >1.E+15 Ohm IEC 60093
Dielectric Strength, shorttime, 1.0mm 29.6 kV/mm IEC 60243-1
Dielectric Strength, in oil, 0.8 mm 35 kV/mm IEC 60243-1
Dielectric Strength, in oil, 1.6 mm 27 kV/mm IEC 60243-1
Dielectric Strength, in oil, 3.2 mm 17 kV/mm IEC 60243-1
Relative Permittivity, 50/60 Hz 2.9 - IEC 60250
Relative Permittivity, 1 MHz 2.8 - IEC 60250
Dissipation Factor, 50/60 Hz 0.001 - IEC 60250
Dissipation Factor, 1 MHz 0.01 - IEC 60250
Comparative Tracking Index 125 V IEC 60112
Comparative Tracking Index, M 100 V IEC 60112
FLAME CHARACTERISTICS Value Unit Standard
UL Recognized, 94V-0 Flame Class Rating (3) 1.5 mm UL 94
Glow Wire Flammability Index 850°C, passes at 1 mm IEC 60695-2-12
Glow Wire Flammability Index 960°C, passes at 1.6 mm IEC 60695-2-12
Oxygen Index (LOI) 40 % ISO 4589
Source GMD, last updated:07/31/1997    

Processing

Parameter    
Injection Molding Value Unit
Drying Temperature 120 °C
Drying Time 2 - 4 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 290 - 320 °C
Nozzle Temperature 280 - 310 °C
Front - Zone 3 Temperature 290 - 320 °C
Middle - Zone 2 Temperature 280 - 310 °C
Rear - Zone 1 Temperature 270 - 300 °C
Hopper Temperature 60 - 80 °C
Mold Temperature 80 - 120 °C
Source GMD, last updated:07/31/1997  

 

For more information please download the datasheet

Sabic Lexan 2814R A High Viscosity, 10% Glass Reinforced, Flame Retardant Grade,Especially Developed To Meet The CSTB 0  Sabic Lexan 2814R.pdf

 

Get The Latest Quotation

 

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

 

Sabic Lexan 2814R A High Viscosity, 10% Glass Reinforced, Flame Retardant Grade,Especially Developed To Meet The CSTB 1Click to consult and get the latest quotation within 24 hours!

 