S-Plastics Lexan 500F resin is 10% glass filled, release grade polycarbonate.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 61 | MPa | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 15 | % | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 100 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 3400 | MPa | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 197 | J/m | ASTM D 256 |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 3.2mm, unannealed | 131 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 142 | °C | ASTM D 648 |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.25 | - | ASTM D 792 |
| Water Absorption, 24 hours | 0.12 | % | ASTM D 570 |
| Mold Shrinkage, flow, 3.2 mm | 0.2 - 0.4 | % | S-Plastics Method |
| Melt Flow Rate, 300°C/1.2 kgf | 6 | g/10 min | ASTM D 1238 |
| Source GMD, last updated:06/18/1999 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 | °C |
| Drying Time | 4 - 6 | hrs |
| Drying Time (Cumulative) | 48 | hrs |
| Melt Temperature | 300 - 325 | °C |
| Mold Temperature | 80 - 115 | °C |
| Source GMD, last updated:06/18/1999 | ||
|
For more information please download the datasheet |
|
 |
S-Plastics Lexan 500F.pdf |
|