S-Plastics Lexan 193 resin is Nonhalogenated. 8.5 MFR. High impact. Thick wall sections. UV-stabilized. Opaques only.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 58 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 50 mm/min | 63 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 50 mm/min | 7 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 115 | % | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 81 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2130 | MPa | ASTM D 790 |
| Hardness, Rockwell M | 68 | - | ASTM D 785 |
| Hardness, Rockwell R | 118 | - | ASTM D 785 |
| Taber Abrasion, CS-17, 1 kg | 20 | mg/1000cy | ASTM D 1044 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 3204 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 747 | J/m | ASTM D 256 |
| Tensile Impact, Type "S" | 420 | kJ/m² | ASTM D 1822 |
| Falling Dart Impact (D 3029), 23°C | 169 | J | ASTM D 3029 |
| THERMAL | Value | Unit | Standard |
| HDT, 0.45 MPa, 6.4 mm, unannealed | 137 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 126 | °C | ASTM D 648 |
| CTE, -40°C to 95°C, flow | 6.48E-05 | 1/°C | ASTM E 831 |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.19 | - | ASTM D 792 |
| Specific Volume | 0.84 | cm³/g | ASTM D 792 |
| Water Absorption, 24 hours | 0.19 | % | ASTM D 570 |
| Water Absorption, equilibrium, 23C | 0.37 | % | ASTM D 570 |
| Water Absorption, equilibrium, 100°C | 0.54 | % | ASTM D 570 |
| Mold Shrinkage, flow, 3.2 mm | 0.5 - 0.7 | % | S-Plastics Method |
| Melt Flow Rate, 300°C/1.2 kgf | 8.5 | g/10 min | ASTM D 1238 |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | 2.5E+17 | Ohm-cm | ASTM D 257 |
| Dielectric Strength, in air, 3.2 mm | 16.3 | kV/mm | ASTM D 149 |
| Relative Permittivity, 1 MHz | 3 | - | ASTM D 150 |
| Dissipation Factor, 50/60 Hz | 0.0009 | - | ASTM D 150 |
| Dissipation Factor, 1 MHz | 0.01 | - | ASTM D 150 |
| Source GMD, last updated:01/04/2000 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 | °C |
| Drying Time | 3 - 4 | hrs |
| Drying Time (Cumulative) | 48 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 310 - 330 | °C |
| Nozzle Temperature | 305 - 325 | °C |
| Front - Zone 3 Temperature | 310 - 330 | °C |
| Middle - Zone 2 Temperature | 300 - 320 | °C |
| Rear - Zone 1 Temperature | 290 - 310 | °C |
| Mold Temperature | 80 - 115 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 40 - 70 | rpm |
| Shot to Cylinder Size | 40 - 60 | % |
| Vent Depth | 0.025 - 0.076 | mm |
| Source GMD, last updated:01/04/2000 | ||
For more information please download the datasheet | |
 | S-Plastics Lexan 193.pdf |