S-Plastics Lexan 135RESIN resin is Lexan 135RESIN_111 is the highest viscosity linear polycarbonate resin powder type. Suitable for extrusion processes. The product
TYPICAL PROPERTIES (1) | |||
MECHANICAL | Value | Unit | Standard |
Tensile Stress, yield, 50 mm/min | 63 | MPa | ISO 527 |
Tensile Stress, break, 50 mm/min | 70 | MPa | ISO 527 |
Tensile Strain, yield, 50 mm/min | 7 | % | ISO 527 |
Tensile Strain, break, 50 mm/min | 120 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 2350 | MPa | ISO 527 |
Flexural Stress, yield, 2 mm/min | 90 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 2300 | MPa | ISO 178 |
THERMAL | Value | Unit | Standard |
CTE, -40°C to 40°C, xflow | 7.E-05 | 1/°C | ISO 11359-2 |
CTE, 23°C to 80°C, flow | 7.E-05 | 1/°C | ISO 11359-2 |
Vicat Softening Temp, Rate B/50 | 144 | °C | ISO 306 |
Vicat Softening Temp, Rate B/120 | 145 | °C | ISO 306 |
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 128 | °C | ISO 75/Ae |
PHYSICAL | Value | Unit | Standard |
Density | 1.2 | g/cm³ | ISO 1183 |
Water Absorption, (23°C/sat) | 0.35 | % | ISO 62 |
Moisture Absorption (23°C / 50% RH) | 0.15 | % | ISO 62 |
Melt Volume Rate, MVR at 300°C/1.2 kg | 3 | cm³/10 min | ISO 1133 |
Source GMD, last updated:10/30/2007 |
Parameter | ||
Profile Extrusion | Value | Unit |
Drying Temperature | 120 | °C |
Drying Time | 2 - 4 | hrs |
Melt Temperature | 270 - 280 | °C |
Barrel - Zone 1 Temperature | 260 - 280 | °C |
Barrel - Zone 2 Temperature | 260 - 280 | °C |
Barrel - Zone 3 Temperature | 260 - 280 | °C |
Barrel - Zone 4 Temperature | 260 - 280 | °C |
Hopper Temperature | 40 - 60 | °C |
Adapter Temperature | 260 - 280 | °C |
Die Temperature | 250 - 260 | °C |
Calibrator Temperature | 70 - 90 | °C |
Source GMD, last updated:10/30/2007 |
For more information please download the datasheet |
|
![]() |
S-Plastics Lexan 135RESIN.pdf |