S-Plastics Lexan 133 resin is Nonhalogenated. 3.5 MFR. UV-stabilized.
TYPICAL PROPERTIES (1) | |||
MECHANICAL | Value | Unit | Standard |
Tensile Stress, yld, Type I, 50 mm/min | 62 | MPa | ASTM D 638 |
Tensile Stress, brk, Type I, 50 mm/min | 65 | MPa | ASTM D 638 |
Tensile Strain, yld, Type I, 50 mm/min | 7 | % | ASTM D 638 |
Tensile Strain, brk, Type I, 50 mm/min | 110 | % | ASTM D 638 |
Flexural Stress, yld, 1.3 mm/min, 50 mm span | 93 | MPa | ASTM D 790 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 2340 | MPa | ASTM D 790 |
Hardness, Rockwell M | 70 | - | ASTM D 785 |
Hardness, Rockwell R | 118 | - | ASTM D 785 |
Taber Abrasion, CS-17, 1 kg | 10 | mg/1000cy | ASTM D 1044 |
IMPACT | Value | Unit | Standard |
Izod Impact, unnotched, 23°C | 3204 | J/m | ASTM D 4812 |
Izod Impact, notched, 23°C | 907 | J/m | ASTM D 256 |
Tensile Impact, Type "S" | 546 | kJ/m² | ASTM D 1822 |
Falling Dart Impact (D 3029), 23°C | 169 | J | ASTM D 3029 |
THERMAL | Value | Unit | Standard |
Vicat Softening Temp, Rate B/50 | 154 | °C | ASTM D 1525 |
HDT, 0.45 MPa, 6.4 mm, unannealed | 137 | °C | ASTM D 648 |
HDT, 1.82 MPa, 6.4 mm, unannealed | 132 | °C | ASTM D 648 |
CTE, -40°C to 95°C, flow | 6.84E-05 | 1/°C | ASTM E 831 |
Specific Heat | 1.25 | J/g-°C | ASTM C 351 |
Thermal Conductivity | 0.19 | W/m-°C | ASTM C 177 |
Relative Temp Index, Elec | 130 | °C | UL 746B |
Relative Temp Index, Mech w/impact | 130 | °C | UL 746B |
Relative Temp Index, Mech w/o impact | 130 | °C | UL 746B |
PHYSICAL | Value | Unit | Standard |
Specific Gravity | 1.2 | - | ASTM D 792 |
Specific Volume | 0.83 | cm³/g | ASTM D 792 |
Density | 1.19 | g/cm³ | ASTM D 792 |
Water Absorption, 24 hours | 0.15 | % | ASTM D 570 |
Water Absorption, equilibrium, 23C | 0.35 | % | ASTM D 570 |
Water Absorption, equilibrium, 100°C | 0.58 | % | ASTM D 570 |
Mold Shrinkage, flow, 3.2 mm | 0.5 - 0.7 | % | S-Plastics Method |
Melt Flow Rate, 300°C/1.2 kgf | 3.5 | g/10 min | ASTM D 1238 |
OPTICAL | Value | Unit | Standard |
Light Transmission | 88 | % | ASTM D 1003 |
Haze | 1 | % | ASTM D 1003 |
Refractive Index | 1.586 | - | ASTM D 542 |
ELECTRICAL | Value | Unit | Standard |
Volume Resistivity | >1.E+17 | Ohm-cm | ASTM D 257 |
Dielectric Strength, in air, 3.2 mm | 14.9 | kV/mm | ASTM D 149 |
Relative Permittivity, 50/60 Hz | 3.17 | - | ASTM D 150 |
Relative Permittivity, 1 MHz | 2.96 | - | ASTM D 150 |
Dissipation Factor, 50/60 Hz | 0.0009 | - | ASTM D 150 |
Dissipation Factor, 1 MHz | 0.01 | - | ASTM D 150 |
Arc Resistance, Tungsten {PLC} | 5 | PLC Code | ASTM D 495 |
Hot Wire Ignition {PLC) | 2 | PLC Code | UL 746A |
High Voltage Arc Track Rate {PLC} | 2 | PLC Code | UL 746A |
High Ampere Arc Ign, surface {PLC} | 4 | PLC Code | UL 746A |
Comparative Tracking Index (UL) {PLC} | 0 | PLC Code | UL 746A |
FLAME CHARACTERISTICS | Value | Unit | Standard |
UL Recognized, 94HB Flame Class Rating (3) | 1.49 | mm | UL 94 |
Source GMD, last updated:01/04/2000 |
Parameter | ||
Injection Molding | Value | Unit |
Drying Temperature | 120 | °C |
Drying Time | 3 - 4 | hrs |
Drying Time (Cumulative) | 48 | hrs |
Maximum Moisture Content | 0.02 | % |
Melt Temperature | 320 - 345 | °C |
Nozzle Temperature | 315 - 340 | °C |
Front - Zone 3 Temperature | 320 - 345 | °C |
Middle - Zone 2 Temperature | 310 - 330 | °C |
Rear - Zone 1 Temperature | 300 - 320 | °C |
Mold Temperature | 80 - 115 | °C |
Back Pressure | 0.3 - 0.7 | MPa |
Screw Speed | 40 - 70 | rpm |
Shot to Cylinder Size | 40 - 60 | % |
Vent Depth | 0.025 - 0.076 | mm |
Source GMD, last updated:01/04/2000 |
For more information please download the datasheet |
|
S-Plastics Lexan 133.pdf |