S-Plastic Lexan 104R 7.0 MFR, For Thicker Sections Without Sinks. Internal Mold Release. FDA Food Contact Compliant

100KG
MOQ
*USD
Price
S-Plastic Lexan 104R  7.0 MFR, For Thicker Sections Without Sinks. Internal Mold Release. FDA Food Contact Compliant
Features Gallery Product Description Request A Quote
Features
Specifications
Melt Volume Rate, MVR At 300°C/1.2 Kg: 6
UL Recognized, 94HB Flame Class Rating (3): 1.47
Basic Infomation
Place of Origin: ——
Brand Name: S-Plastic Lexan
Certification: COA/ICP Test/Rohs/MSDS
Model Number: 104R
Payment & Shipping Terms
Packaging Details: 25KG/BAG
Delivery Time: To be negotiated
Payment Terms: L/C, T/T, Western Union, MoneyGram
Supply Ability: To be negotiated
Product Description

S-Plastics Lexan  104R resin isUL rated HB. 200 series recommended when V-2 rating required. 7.0 MFR, for thicker sections without sinks. Internal mold release. FDA food contact compliant in limited colors.Effective January 15th, 2007 this grade will no longer be supported with biocompatibility information and should not be used for medical applications which require biocompatibility. Alternative grade HP6.

 


Property

TYPICAL PROPERTIES (1)      
MECHANICAL Value Unit Standard
Tensile Stress, yld, Type I, 50 mm/min 62 MPa ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min 68 MPa ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min 7 % ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min 135 % ASTM D 638
Tensile Modulus, 5 mm/min 2310 MPa ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span 97 MPa ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span 2340 MPa ASTM D 790
Hardness, Rockwell M 70 - ASTM D 785
Hardness, Rockwell R 118 - ASTM D 785
Taber Abrasion, CS-17, 1 kg 10 mg/1000cy ASTM D 1044
Taber Abrasion, CS-17, 1 kg 10 mg/1000cy S-Plastics Method
Tensile Stress, yield, 50 mm/min 63 MPa ISO 527
Tensile Stress, break, 50 mm/min 70 MPa ISO 527
Tensile Strain, yield, 50 mm/min 6 % ISO 527
Tensile Strain, break, 50 mm/min 120 % ISO 527
Tensile Modulus, 1 mm/min 2350 MPa ISO 527
Flexural Stress, yield, 2 mm/min 90 MPa ISO 178
Flexural Modulus, 2 mm/min 2300 MPa ISO 178
Hardness, H358/30 95 MPa ISO 2039-1
IMPACT Value Unit Standard
Izod Impact, unnotched, 23°C 3204 J/m ASTM D 4812
Izod Impact, notched, 23°C 907 J/m ASTM D 256
Izod Impact, notched, -30°C 139 J/m ASTM D 256
Tensile Impact, Type "S" 630 kJ/m² ASTM D 1822
Falling Dart Impact (D 3029), 23°C 169 J ASTM D 3029
Instrumented Impact Total Energy, 23°C 65 J ASTM D 3763
Izod Impact, notched 80*10*4 +23°C 65 kJ/m² ISO 180/1A
Izod Impact, notched 80*10*4 -30°C 10 kJ/m² ISO 180/1A
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm 95 kJ/m² ISO 179/1eA
Charpy Impact, notched, 23°C 35 kJ/m² ISO 179/2C
THERMAL Value Unit Standard
Vicat Softening Temp, Rate B/50 154 °C ASTM D 1525
HDT, 0.45 MPa, 6.4 mm, unannealed 137 °C ASTM D 648
HDT, 1.82 MPa, 6.4 mm, unannealed 132 °C ASTM D 648
CTE, -40°C to 40°C, flow 6.2E-05 1/°C ASTM E 831
CTE, -40°C to 40°C, xflow 5.7E-05 1/°C ASTM E 831
Specific Heat 1.25 J/g-°C ASTM C 351
Thermal Conductivity 0.19 W/m-°C ASTM C 177
Thermal Conductivity 0.2 W/m-°C ISO 8302
CTE, -40°C to 40°C, flow 6.E-05 1/°C ISO 11359-2
CTE, -40°C to 40°C, xflow 6.E-05 1/°C ISO 11359-2
CTE, 23°C to 80°C, flow 7.E-05 1/°C ISO 11359-2
Ball Pressure Test, 125°C +/- 2°C PASSES - IEC 60695-10-2
Ball Pressure Test, approximate maximum 140 °C IEC 60695-10-2
Vicat Softening Temp, Rate B/50 144 °C ISO 306
Vicat Softening Temp, Rate B/120 145 °C ISO 306
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm 138 °C ISO 75/Be
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm 127 °C ISO 75/Ae
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm 124 °C ISO 75/Af
Relative Temp Index, Elec 130 °C UL 746B
Relative Temp Index, Mech w/impact 130 °C UL 746B
Relative Temp Index, Mech w/o impact 130 °C UL 746B
PHYSICAL Value Unit Standard
Specific Gravity 1.2 - ASTM D 792
Specific Volume 0.83 cm³/g ASTM D 792
Density 1.19 g/cm³ ASTM D 792
Water Absorption, 24 hours 0.15 % ASTM D 570
Water Absorption, equilibrium, 23C 0.35 % ASTM D 570
Water Absorption, equilibrium, 100°C 0.58 % ASTM D 570
Mold Shrinkage, flow, 3.2 mm 0.5 - 0.7 % S-Plastics Method
Melt Flow Rate, 300°C/1.2 kgf 7 g/10 min ASTM D 1238
Density 1.2 g/cm³ ISO 1183
Water Absorption, (23°C/sat) 0.35 % ISO 62
Moisture Absorption (23°C / 50% RH) 0.15 % ISO 62
Melt Volume Rate, MVR at 220°C/5.0 kg 4 cm³/10 min ISO 1133
Melt Volume Rate, MVR at 300°C/1.2 kg 6 cm³/10 min ISO 1133
OPTICAL Value Unit Standard
Light Transmission 88 % ASTM D 1003
Haze 1 % ASTM D 1003
Refractive Index 1.586 - ASTM D 542
Refractive Index 1.586 - ISO 489
ELECTRICAL Value Unit Standard
Volume Resistivity >1.E+17 Ohm-cm ASTM D 257
Dielectric Strength, in air, 3.2 mm 14.9 kV/mm ASTM D 149
Relative Permittivity, 50/60 Hz 3.17 - ASTM D 150
Relative Permittivity, 1 MHz 2.96 - ASTM D 150
Dissipation Factor, 50/60 Hz 0.0009 - ASTM D 150
Dissipation Factor, 1 MHz 0.01 - ASTM D 150
Hot Wire Ignition {PLC) 2 PLC Code UL 746A
High Voltage Arc Track Rate {PLC} 2 PLC Code UL 746A
High Ampere Arc Ign, surface {PLC} 1 PLC Code UL 746A
Comparative Tracking Index (UL) {PLC} 2 PLC Code UL 746A
Dielectric Strength, in oil, 3.2 mm 17 kV/mm IEC 60243-1
Relative Permittivity, 50/60 Hz 2.7 - IEC 60250
Relative Permittivity, 1 MHz 2.7 - IEC 60250
Dissipation Factor, 50/60 Hz 0.001 - IEC 60250
Dissipation Factor, 1 MHz 0.01 - IEC 60250
FLAME CHARACTERISTICS Value Unit Standard
UL Recognized, 94HB Flame Class Rating (3) 1.47 mm UL 94
Glow Wire Flammability Index 850°C, passes at 1 mm IEC 60695-2-12
Oxygen Index (LOI) 25 % ISO 4589
Source GMD, last updated:12/01/2006    

Processing

Parameter    
Injection Molding Value Unit
Drying Temperature 120 °C
Drying Time 3 - 4 hrs
Drying Time (Cumulative) 48 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 310 - 330 °C
Nozzle Temperature 305 - 325 °C
Front - Zone 3 Temperature 310 - 330 °C
Middle - Zone 2 Temperature 300 - 320 °C
Rear - Zone 1 Temperature 290 - 310 °C
Mold Temperature 80 - 115 °C
Back Pressure 0.3 - 0.7 MPa
Screw Speed 40 - 70 rpm
Shot to Cylinder Size 40 - 60 %
Vent Depth 0.025 - 0.076 mm
Source GMD, last updated:12/01/2006  

 


 

For more information please download the datasheet

S-Plastic Lexan 104R  7.0 MFR, For Thicker Sections Without Sinks. Internal Mold Release. FDA Food Contact Compliant 0  S-Plastics Lexan 104R.pdf

 

Get The Latest Quotation

 

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

 

S-Plastic Lexan 104R  7.0 MFR, For Thicker Sections Without Sinks. Internal Mold Release. FDA Food Contact Compliant 1Click to consult and get the latest quotation within 24 hours!

 

S-Plastics lexan pc products

 

Free Talk 24hours

Recommended Products
Get in touch with us
Tel : 86-13925273675
Characters Remaining(20/3000)