S-Plastics Lexan503resin adalah10% GR PC. Kombinasi optimal modulus tinggi ditambah kekuatan benturan yang sangat baik dan tahan api.
Properti Tipikal (1) | |||
Mekanis | Nilai | Satuan | Standar |
Tekanan tarik, yld, tipe I, 5 mm/menit | 66 | MPa | ASTM D 638 |
Tekanan tarik, brk, tipe I, 5 mm/menit | 55 | MPa | ASTM D 638 |
Tekanan tarik, yld, tipe I, 5 mm/menit | 8 | % | ASTM D 638 |
Tekanan tarik, brk, tipe I, 5 mm/menit | 15 | % | ASTM D 638 |
Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 103 | MPa | ASTM D 790 |
Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 3440 | MPa | ASTM D 790 |
Kekerasan, Rockwell M | 85 | - | ASTM D 785 |
Kekerasan, Rockwell R | 124 | - | ASTM D 785 |
Taber Abrasion, CS-17, 1 kg | 11 | mg/1000cy | ASTM D 1044 |
Dampak | Nilai | Satuan | Standar |
Izod Dampak, tidak diukir, 23°C | 2136 | J/m | ASTM D 4812 |
Izod Dampak, bertanduk, 23°C | 106 | J/m | ASTM D 256 |
Dampak tegangan, tipe "S" | 157 | kJ/m2 | ASTM D 1822 |
Dampak panah jatuh (D 3029), 23°C | 101 | J | ASTM D 3029 |
Termal | Nilai | Satuan | Standar |
Vicat Softening Temperature, Tingkat B/50 | 154 | °C | ASTM D 1525 |
HDT, 0,45 MPa, 6,4 mm, tidak diiris | 146 | °C | ASTM D 648 |
HDT, 1,82 MPa, 6,4 mm, tidak diiris | 142 | °C | ASTM D 648 |
CTE, -40°C sampai 95°C, aliran | 3.24E-05 | 1/°C | ASTM E 831 |
Panas spesifik | 1.21 | J/g-°C | ASTM C 351 |
Konduktivitas Termal | 0.2 | W/m-°C | ASTM C 177 |
Indeks suhu relatif, Elec | 120 | °C | UL 746B |
Indeks suhu relatif, Mech w/impact | 110 | °C | UL 746B |
Indeks suhu relatif, Mech tanpa dampak | 125 | °C | UL 746B |
FISIK | Nilai | Satuan | Standar |
Gravitasi Spesifik | 1.25 | - | ASTM D 792 |
Volume Spesifik | 0.8 | cm3/g | ASTM D 792 |
Kepadatan | 1.245 | g/cm3 | ASTM D 792 |
Penyerapan air, 24 jam | 0.12 | % | ASTM D 570 |
Penyerapan air, keseimbangan, 23C | 0.31 | % | ASTM D 570 |
Penyusutan jamur, aliran, 3,2 mm | 0.2 - 0.4 | % | Metode S-Plastics |
Listrik | Nilai | Satuan | Standar |
Resistivitas Volume | >1.E+17 | Ohm-cm | ASTM D 257 |
Kekuatan dielektrik, di udara, 3,2 mm | 17.7 | kV/mm | ASTM D 149 |
Permittivitas relatif, 50/60 Hz | 3.1 | - | ASTM D 150 |
Permittivitas Relatif, 1 MHz | 3.05 | - | ASTM D 150 |
Faktor Dissipasi, 50/60 Hz | 0.0008 | - | ASTM D 150 |
Faktor Dissipasi, 1 MHz | 0.0075 | - | ASTM D 150 |
Resistensi busur, Tungsten {PLC} | 7 | Kode PLC | ASTM D 495 |
Pemicu Hot Wire {PLC) | 1 | Kode PLC | UL 746A |
Tingkat Jalur Arc Tegangan Tinggi {PLC} | 3 | Kode PLC | UL 746A |
High Ampere Arc Ign, permukaan {PLC} | 1 | Kode PLC | UL 746A |
Indeks Pelacakan Perbandingan (UL) {PLC} | 4 | Kode PLC | UL 746A |
Karakteristik Api | Nilai | Satuan | Standar |
UL diakui, 94V-0 Flame Class Rating (3) | 1.52 | mm | UL 94 |
UL diakui, 94-5VA rating (3) | 2.99 | mm | UL 94 |
Indeks Oksigen (LOI) | 36 | % | ASTM D 2863 |
Sinar UV, paparan air/pencelupan | F1 | - | UL 746C |
Sumber GMD, terakhir diperbarui:12/29/1999 |
Parameter | ||
Pencetakan Injeksi | Nilai | Satuan |
Suhu Pengeringan | 120 | °C |
Waktu Pengeringan | 3 - 4 | jam |
Waktu pengeringan (kumulatif) | 48 | jam |
Kandungan Kelembaban Maksimal | 0.02 | % |
Suhu Peleburan | 310 - 330 | °C |
Suhu Nozzle | 305 - 325 | °C |
Suhu depan - Zona 3 | 310 - 330 | °C |
Tengah - Zona 2 Suhu | 300 - 320 | °C |
Bagian belakang - Zona 1 Suhu | 290 - 310 | °C |
Suhu Cetakan | 80 - 115 | °C |
Tekanan Belakang | 0.3 - 0.7 | MPa |
Kecepatan sekrup | 40 - 70 | rpm |
Menembak untuk ukuran silinder | 40 - 60 | % |
Kedalaman ventilasi | 0.025 - 0.076 | mm |
Sumber GMD, terakhir diperbarui:12/29/1999 |
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
![]() |
S-Plastics Lexan 503.pdf |