S-Plastics Lexan3433Rresin adalah30% GR, memberikan sifat mekanik yang lebih baik, stabil UV, pelepasan jamur internal.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 131 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 3 | % | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 158 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 7580 | MPa | ASTM D 790 |
| Kekerasan, Rockwell M | 92 | - | ASTM D 785 |
| Kekerasan, Rockwell R | 121 | - | ASTM D 785 |
| Taber Abrasion, CS-17, 1 kg | 24 | mg/1000cy | ASTM D 1044 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 1121 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 106 | J/m | ASTM D 256 |
| Dampak tegangan, tipe "S" | 67 | kJ/m2 | ASTM D 1822 |
| Dampak panah jatuh (D 3029), 23°C | 5 | J | ASTM D 3029 |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 154 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 6,4 mm, tidak diiris | 151 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 146 | °C | ASTM D 648 |
| CTE, -40°C sampai 95°C, aliran | 2.16E-05 | 1/°C | ASTM E 831 |
| Panas spesifik | 1.13 | J/g-°C | ASTM C 351 |
| Konduktivitas Termal | 0.22 | W/m-°C | ASTM C 177 |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.43 | - | ASTM D 792 |
| Volume Spesifik | 0.69 | cm3/g | ASTM D 792 |
| Kepadatan | 1.439 | g/cm3 | ASTM D 792 |
| Penyerapan air, 24 jam | 0.14 | % | ASTM D 570 |
| Penyerapan air, keseimbangan, 23C | 0.26 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 3,2 mm | 0.1 - 0.3 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 300°C/5,0 kgf | 19 | g/10 menit | ASTM D 1238 |
| Sumber GMD, terakhir diperbarui:12/29/1999 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 3 - 4 | jam |
| Waktu pengeringan (kumulatif) | 48 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 315 - 340 | °C |
| Suhu Nozzle | 310 - 330 | °C |
| Suhu depan - Zona 3 | 315 - 340 | °C |
| Tengah - Zona 2 Suhu | 305 - 325 | °C |
| Bagian belakang - Zona 1 Suhu | 295 - 315 | °C |
| Suhu Cetakan | 80 - 115 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 40 - 70 | rpm |
| Menembak untuk ukuran silinder | 40 - 60 | % |
| Kedalaman ventilasi | 0.025 - 0.076 | mm |
| Sumber GMD, terakhir diperbarui:12/29/1999 | ||