Sabic Lexan224Rresin adalahHanya untuk aplikasi yang ada. 17,5 MFR, untuk bagian-bagian kecil dan rumit.
Properti Tipikal (1) | |||
Mekanis | Nilai | Satuan | Standar |
Tekanan tarik, yld, tipe I, 50 mm/menit | 62 | MPa | ASTM D 638 |
Tekanan tarik, brk, tipe I, 50 mm/menit | 68 | MPa | ASTM D 638 |
Tekanan tarik, yld, tipe I, 50 mm/menit | 7 | % | ASTM D 638 |
Tekanan tarik, brk, tipe I, 50 mm/menit | 125 | % | ASTM D 638 |
Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 96 | MPa | ASTM D 790 |
Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2340 | MPa | ASTM D 790 |
Kekerasan, Rockwell M | 70 | - | ASTM D 785 |
Kekerasan, Rockwell R | 118 | - | ASTM D 785 |
Taber Abrasion, CS-17, 1 kg | 10 | mg/1000cy | ASTM D 1044 |
Dampak | Nilai | Satuan | Standar |
Izod Dampak, tidak diukir, 23°C | 3204 | J/m | ASTM D 4812 |
Izod Dampak, bertanduk, 23°C | 694 | J/m | ASTM D 256 |
Dampak tegangan, tipe "S" | 546 | kJ/m2 | ASTM D 1822 |
Dampak panah jatuh (D 3029), 23°C | 169 | J | ASTM D 3029 |
Termal | Nilai | Satuan | Standar |
Vicat Softening Temperature, Tingkat B/50 | 154 | °C | ASTM D 1525 |
HDT, 0,45 MPa, 6,4 mm, tidak diiris | 137 | °C | ASTM D 648 |
HDT, 1,82 MPa, 6,4 mm, tidak diiris | 129 | °C | ASTM D 648 |
CTE, -40°C sampai 95°C, aliran | 6.84E-05 | 1/°C | ASTM E 831 |
Panas spesifik | 1.25 | J/g-°C | ASTM C 351 |
Konduktivitas Termal | 0.25 | W/m-°C | ASTM C 177 |
Indeks suhu relatif, Elec | 130 | °C | UL 746B |
Indeks suhu relatif, Mech w/impact | 130 | °C | UL 746B |
Indeks suhu relatif, Mech tanpa dampak | 130 | °C | UL 746B |
FISIK | Nilai | Satuan | Standar |
Gravitasi Spesifik | 1.2 | - | ASTM D 792 |
Volume Spesifik | 0.83 | cm3/g | ASTM D 792 |
Kepadatan | 1.19 | g/cm3 | ASTM D 792 |
Penyerapan air, 24 jam | 0.15 | % | ASTM D 570 |
Penyerapan air, keseimbangan, 23C | 0.35 | % | ASTM D 570 |
Penyerapan air, keseimbangan, 100°C | 0.58 | % | ASTM D 570 |
Penyusutan jamur, aliran, 3,2 mm | 0.5 - 0.7 | % | Metode SABIC |
Tingkat Aliran Peleburan, 300°C/1,2 kgf | 17.5 | g/10 menit | ASTM D 1238 |
Optik | Nilai | Satuan | Standar |
Transmisi Cahaya | 88 | % | ASTM D 1003 |
Kabut | 1 | % | ASTM D 1003 |
Indeks Refraksi | 1.586 | - | ASTM D 542 |
Listrik | Nilai | Satuan | Standar |
>1.E+17 | Ohm-cm | ASTM D 257 | |
Kekuatan dielektrik, di udara, 3,2 mm | 14.9 | kV/mm | ASTM D 149 |
Permittivitas relatif, 50/60 Hz | 3.17 | - | ASTM D 150 |
Permittivitas Relatif, 1 MHz | 2.96 | - | ASTM D 150 |
Faktor Dissipasi, 50/60 Hz | 0.0009 | - | ASTM D 150 |
Faktor Dissipasi, 1 MHz | 0.01 | - | ASTM D 150 |
Pemicu Hot Wire {PLC) | 2 | Kode PLC | UL 746A |
Tingkat Jalur Arc Tegangan Tinggi {PLC} | 2 | Kode PLC | UL 746A |
High Ampere Arc Ign, permukaan {PLC} | 1 | Kode PLC | UL 746A |
Indeks Pelacakan Perbandingan (UL) {PLC} | 2 | Kode PLC | UL 746A |
Karakteristik Api | Nilai | Satuan | Standar |
UL diakui, 94V-2 Flame Class Rating (3) | 1.47 | mm | UL 94 |
UL diakui, 94V-0 Flame Class Rating (3) | 5.99 | mm | UL 94 |
Sumber GMD, terakhir diperbarui:01/04/2000 |
Parameter | ||
Pencetakan Injeksi | Nilai | Satuan |
Suhu Pengeringan | 120 | °C |
Waktu Pengeringan | 3 - 4 | jam |
Waktu pengeringan (kumulatif) | 48 | jam |
Kandungan Kelembaban Maksimal | 0.02 | % |
Suhu Peleburan | 280 - 305 | °C |
Suhu Nozzle | 275 - 300 | °C |
Suhu depan - Zona 3 | 280 - 305 | °C |
Tengah - Zona 2 Suhu | 270 - 295 | °C |
Bagian belakang - Zona 1 Suhu | 260 - 280 | °C |
Suhu Cetakan | 70 - 95 | °C |
Tekanan Belakang | 0.3 - 0.7 | MPa |
Kecepatan sekrup | 40 - 70 | rpm |
Menembak untuk ukuran silinder | 40 - 60 | % |
Kedalaman ventilasi | 0.025 - 0.076 | mm |
Sumber GMD, terakhir diperbarui:01/04/2000 |
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
Sabic Lexan 224r.pdf |
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
Klik untuk berkonsultasi dan dapatkan penawaran terbaru dalam waktu 24 jam! |