Sabic Lexan223HSRresin adalahAliran mudah, tahan api, UV stabil, super release grade polikarbonat.
Properti Tipikal (1) | |||
Mekanis | Nilai | Satuan | Standar |
Tekanan tarik, yld, tipe I, 50 mm/menit | 65 | MPa | ASTM D 638 |
Tekanan tarik, brk, tipe I, 50 mm/menit | 143 | % | ASTM D 638 |
Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 97 | MPa | ASTM D 790 |
Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2300 | MPa | ASTM D 790 |
Dampak | Nilai | Satuan | Standar |
Izod Dampak, bertanduk, 23°C | 801 | J/m | ASTM D 256 |
Termal | Nilai | Satuan | Standar |
HDT, 1,82 MPa, 3,2 mm, tidak diiris | 123 | °C | ASTM D 648 |
HDT, 1,82 MPa, 6,4 mm, tidak diiris | 133 | °C | ASTM D 648 |
FISIK | Nilai | Satuan | Standar |
Gravitasi Spesifik | 1.2 | - | ASTM D 792 |
Penyerapan air, 24 jam | 0.15 | % | ASTM D 570 |
Penyusutan jamur, aliran, 3,2 mm | 0.5 - 0.7 | % | Metode SABIC |
Tingkat Aliran Peleburan, 300°C/1,2 kgf | 18 | g/10 menit | ASTM D 1238 |
Karakteristik Api | Nilai | Satuan | Standar |
UL diakui, 94HB Flame Class Rating (3) | 1.5 | mm | UL 94 |
Sumber GMD, terakhir diperbarui:06/18/1999 |
Parameter | ||
Pencetakan Injeksi | Nilai | Satuan |
Suhu Pengeringan | 120 | °C |
Waktu Pengeringan | 3 - 4 | jam |
Waktu pengeringan (kumulatif) | 48 | jam |
Suhu Peleburan | 280 - 305 | °C |
Suhu Cetakan | 70 - 95 | °C |
Sumber GMD, terakhir diperbarui:06/18/1999 |
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
Sabic Lexan 223HSR.pdf |
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
Klik untuk berkonsultasi dan dapatkan penawaran terbaru dalam waktu 24 jam! |