Sabic Lexan121resin adalahUL memberi rating HB pada 10/97. seri 200 direkomendasikan ketika rating V-2 diperlukan. Nonhalogenated. 17.5 MFR, untuk bagian kecil yang rumit.
Properti Tipikal (1) | |||
Mekanis | Nilai | Satuan | Standar |
Tekanan tarik, yld, tipe I, 50 mm/menit | 62 | MPa | ASTM D 638 |
Tekanan tarik, brk, tipe I, 50 mm/menit | 68 | MPa | ASTM D 638 |
Tekanan tarik, yld, tipe I, 50 mm/menit | 7 | % | ASTM D 638 |
Tekanan tarik, brk, tipe I, 50 mm/menit | 125 | % | ASTM D 638 |
Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 96 | MPa | ASTM D 790 |
Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2340 | MPa | ASTM D 790 |
Kekerasan, Rockwell M | 70 | - | ASTM D 785 |
Kekerasan, Rockwell R | 118 | - | ASTM D 785 |
Taber Abrasion, CS-17, 1 kg | 10 | mg/1000cy | ASTM D 1044 |
Dampak | Nilai | Satuan | Standar |
Izod Dampak, tidak diukir, 23°C | 3204 | J/m | ASTM D 4812 |
Izod Dampak, bertanduk, 23°C | 694 | J/m | ASTM D 256 |
Dampak tegangan, tipe "S" | 546 | kJ/m2 | ASTM D 1822 |
Dampak panah jatuh (D 3029), 23°C | 169 | J | ASTM D 3029 |
Energi Dampak Instrumen @ puncak, 23°C | 62 | J | ASTM D 3763 |
Termal | Nilai | Satuan | Standar |
Vicat Softening Temperature, Tingkat B/50 | 154 | °C | ASTM D 1525 |
HDT, 0,45 MPa, 6,4 mm, tidak diiris | 137 | °C | ASTM D 648 |
HDT, 1,82 MPa, 6,4 mm, tidak diiris | 129 | °C | ASTM D 648 |
CTE, -40°C sampai 95°C, aliran | 6.84E-05 | 1/°C | ASTM E 831 |
Panas spesifik | 1.25 | J/g-°C | ASTM C 351 |
Konduktivitas Termal | 0.25 | W/m-°C | ASTM C 177 |
Indeks suhu relatif, Elec | 130 | °C | UL 746B |
Indeks suhu relatif, Mech w/impact | 130 | °C | UL 746B |
Indeks suhu relatif, Mech tanpa dampak | 130 | °C | UL 746B |
FISIK | Nilai | Satuan | Standar |
Gravitasi Spesifik | 1.2 | - | ASTM D 792 |
Volume Spesifik | 0.83 | cm3/g | ASTM D 792 |
Kepadatan | 1.19 | g/cm3 | ASTM D 792 |
Penyerapan air, 24 jam | 0.15 | % | ASTM D 570 |
Penyerapan air, keseimbangan, 23C | 0.35 | % | ASTM D 570 |
Penyerapan air, keseimbangan, 100°C | 0.58 | % | ASTM D 570 |
Penyusutan jamur, aliran, 3,2 mm | 0.5 - 0.7 | % | Metode SABIC |
Tingkat Aliran Peleburan, 300°C/1,2 kgf | 17.5 | g/10 menit | ASTM D 1238 |
Optik | Nilai | Satuan | Standar |
Transmisi Cahaya | 88 | % | ASTM D 1003 |
Kabut | 1 | % | ASTM D 1003 |
Indeks Refraksi | 1.586 | - | ASTM D 542 |
Listrik | Nilai | Satuan | Standar |
Resistivitas Volume | >1.E+17 | Ohm-cm | ASTM D 257 |
Kekuatan dielektrik, di udara, 3,2 mm | 14.9 | kV/mm | ASTM D 149 |
Permittivitas relatif, 50/60 Hz | 3.17 | - | ASTM D 150 |
Permittivitas Relatif, 1 MHz | 2.96 | - | ASTM D 150 |
Faktor Dissipasi, 50/60 Hz | 0.0009 | - | ASTM D 150 |
Faktor Dissipasi, 1 MHz | 0.01 | - | ASTM D 150 |
Pemicu Hot Wire {PLC) | 2 | Kode PLC | UL 746A |
Tingkat Jalur Arc Tegangan Tinggi {PLC} | 2 | Kode PLC | UL 746A |
High Ampere Arc Ign, permukaan {PLC} | 1 | Kode PLC | UL 746A |
Indeks Pelacakan Perbandingan (UL) {PLC} | 2 | Kode PLC | UL 746A |
Karakteristik Api | Nilai | Satuan | Standar |
UL diakui, 94HB Flame Class Rating (3) | 0.71 | mm | UL 94 |
CSA (Lihat File untuk daftar lengkap) | LS88480 | File No. | CSA terdaftar |
Daftar Panel Radiant | Ya. | - | Uji UL |
Sinar UV, paparan air/pencelupan | F2 | - | UL 746C |
Sumber GMD, terakhir diperbarui:01/04/2000 |
Parameter | ||
Pencetakan Injeksi | Nilai | Satuan |
Suhu Pengeringan | 120 | °C |
Waktu Pengeringan | 3 - 4 | jam |
Waktu pengeringan (kumulatif) | 48 | jam |
Kandungan Kelembaban Maksimal | 0.02 | % |
Suhu Peleburan | 280 - 305 | °C |
Suhu Nozzle | 275 - 300 | °C |
Suhu depan - Zona 3 | 280 - 305 | °C |
Tengah - Zona 2 Suhu | 270 - 295 | °C |
Bagian belakang - Zona 1 Suhu | 260 - 280 | °C |
Suhu Cetakan | 70 - 95 | °C |
Tekanan Belakang | 0.3 - 0.7 | MPa |
Kecepatan sekrup | 40 - 70 | rpm |
Menembak untuk ukuran silinder | 40 - 60 | % |
Kedalaman ventilasi | 0.025 - 0.076 | mm |
Sumber GMD, terakhir diperbarui:01/04/2000 |
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
Sabic Lexan 121.pdf |